Anisoprint Clear PETG Filament,1.75mm, 600 cc

₹11699.00

Anisoprint Clear PETG Filament,1.75mm, 600 cc
(0 reviews)
Product Features

• Low moisture absorption

• High interlayer strength

• Low shrinkage

• Specially designed for Anisoprint CFC technology

- 14%
₹10069.00
MRP : ₹
11699.00

Estimated delivery time      4-5 business days

Free shipping on All orders

Cash on Delivery Available

- +
Add to cart
Add to wishlist Remove from wishlist Compare Ask a question Share

Guarantee Safe Checkout:

  • card
  • card
  • card
  • card
Frequently Bought Together
img-product
eSUN Hard-Tough Resin, Grey, 0.5kg
₹2329.00 ₹4658.00
img-product
eSUN ePAHT-CF 3D Printing Filament Natural,1.75mm, Gross Weight-1kg
₹5899.00 ₹11798.00
img-product
Circular Laser Head 5.5w For TTC450
₹8199.00 ₹10079.00
img-product
Anycubic ABS Like Pro 2 Resin (Grey) 1Kg
₹1899.00 ₹3798.00
Total price:
₹60.00
Anisoprint Clear PETG Filament,1.75mm, 600 cc
Add to cart
  • The Clear PETG features high layer adhesion and low shrinkage which results in strong thin-walled parts with excellent mechanical and physical properties, such as a wide range of working temperatures (-40 °C to +70 °C), chemical resistance, high durability, and others.
  • It is recommended to be printed with a plastic extruder at 235–240 °C with the print speed of 40–55 mm/s.
  • For the first layer and the external shells, it is better to reduce the speed to 25 mm/s or lower for better first layer adhesion and a smoother surface finish. The recommended print bed temperature is 45–60 °C.
  • The Anisoprint Clear PETG features low moisture absorption which means it can be stored without drying for weeks and printed without an active dryer.
  • If the air humidity is high and the filament has absorbed moisture, drying for 2–4 hours at 60 °C is recommended.
  • Low moisture absorption High interlayer strength Low shrinkage Specially designed for Anisoprint CFC technology.
  • ending modulus (X-Y) : 2.06 GPa
  • Bending strength (X-Y) : 76.1 MPa
  • Color name : Transparent
  • Compressive modulus (Z-X) : 1.81 GPa
  • Compressive strength (Z-X) : 51.7 MPa
  • Density : 1.3 g/sm³
  • Diameter : 1.75 mm
  • Elongation at break : 2.41%
  • Filament volume : 600 cc
  • Filament weight : approx. 750 g
  • HDT (0.45 MPa) : 71 °C
  • Notched Сharpy impact : 4.17 KJ/m²
  • Tensile strength (X-Y) : 36.5 MPa
  • Tensile strength (Z-X) : 33.6 MPa
  • Vicat softening temperature : 80 °C
  • Young’s modulus (X-Y) : 1.12 GPa
  • Young’s modulus (Z-X) : 1.73 GPa
Customer review
  • (0)
0.0 /5.0
5
0
4
0
3
0
2
0
1
0
Write a review
Write a review

Your email address will not be published. Required fields are marked *

Your rating *
Ask a Question
Your name*
Your phone number
Your email*
Message*
Provide Contact for Notification
Your name*
Your phone number
Your email*
Share
Copy